X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 - Spesifikasi & Aplikasi
X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 - Spesifikasi & Aplikasi
- SAE AMS 5342E (2006) - Keluli, Tahan Kakisan, Tuangan Pelaburan 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenisasi, Penyelesaian dan Pemendakan Haba Dirawat (H1100 ) 130 ksi (896 MPa) Kekuatan Tegangan (17-4)
- SAE AMS 5343E (2006) - Keluli, Tahan Kakisan, Tuangan Pelaburan 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenisasi, Penyelesaian dan Pemendakan Haba Dirawat (H1000 ) 150 ksi (1034 MPa) Kekuatan Tegangan (17-4)
- SAE AMS 5344F (2007) - Keluli, Tahan Kakisan, Tuangan Pelaburan 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Penghomogenan, Penyelesaian dan Kerpasan Dirawat Haba (H900) 180 ksi (1241 MPa) Kekuatan Tegangan (17-4)
- SAE AMS 5604G (2013) - Keluli, Kalis Kakisan, Lembaran, Jalur dan Plat 16.5Cr - 4.0Ni - 4.0Cu {{9} }.30Cb Solution Haba Dirawat, Kerpasan Boleh Mengeras
- SAE AMS 5622F (2013) - Keluli, Tahan Kakisan, Bar, Wayar, Penempaan, Tiub dan Gelang 16Cr - 4.0Ni - 0.30Cb { {9}}.0Cu Solution Haba Dirawat, Kerpasan Mengeras Elektrod Boleh Habis Dicairkan Semula
- SAE AMS 5643/H1150 (2013) - Keluli, Tahan Kakisan, Bar, Wayar, Penempaan, Tiub dan Gelang 16Cr – 4.0Ni – 0.30Cb (Nb ) – Penyelesaian 4.0Cu dan Dirawat Haba Kerpasan (H1150)
- SAE AMS 5643S (2013) - Keluli, Tahan Kakisan, Bar, Wayar, Penempaan, Tiub dan Gelang 16Cr - 4.0Ni - 0.30Cb { {9}}.0Penyelesaian Cu Dirawat Haba, Kerpasan Boleh Mengeras
- MS 10088-2 - Keluli tahan karat. Keadaan penghantaran teknikal untuk kepingan/plat dan jalur keluli tahan kakisan untuk tujuan umum
Keluli, Tahan Kakisan, Tuangan Pelaburan 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Penghomogenan, Penyelesaian dan Kerpasan Dirawat Haba (H1100) 130 ksi (896 MPa) Kekuatan Tegangan (17-4)
Komposisi kimia(peratus berat ) X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 gred: kepada SAE AMS 5342E (2006)
| elemen | Min.（ Lebih besar daripada atau sama dengan ） | Maks.（ Kurang daripada atau sama dengan ） | serupa | Kenyataan |
|---|
| C | - | 0.07 |
|
|
| Si | - | 1.00 |
|
|
| Mn | - | 1.00 |
|
|
| Cr | 15.00 | 17.50 |
|
|
| Ni | 3.00 | 5.00 |
|
|
| Cu | 3.00 | 5.00 |
|
|
| Nb | 0.15 | 1.45 |
|
|
Sifat mekanikal gred X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 gred: hingga SAE AMS 5342E (2006)
Kekuatan Hasil,Rp 0.2(MPa)
| keadaan | Min | Maks | serupa | Catatan |
|---|
| H900 | 1170 |
|
|
|
| H925 | 1070 |
|
|
|
| H1025 | 1000 |
|
|
|
| H1075 | 860 |
|
|
|
| H1100 | 795 |
|
|
|
| H1150 | 725 |
|
|
|
| H1150M | 520 |
|
|
|
| H1150D | 725 |
|
|
|
Kekuatan Tegangan, Rm(MPa)
| keadaan | Min | Maks | serupa | Catatan |
|---|
| H900 | 1310 |
|
|
|
| H925 | 1170 |
|
|
|
| H1025 | 1070 |
|
|
|
| H1075 | 1000 |
|
|
|
| H1100 | 965 |
|
|
|
| H1150 | 930 |
|
|
|
| H1150M | 795 |
|
|
|
| H1150D | 860 |
|
|
|
Kesan,Kv/Ku(J)
| keadaan | Min | Maks | serupa | Catatan |
|---|
| H925 | 6.8 |
|
| AKV 21 darjah |
| H1025 | 20 |
|
| AKV 21 darjah |
| H1075 | 27 |
|
| AKV 21 darjah |
| H1100 | 34 |
|
| AKV 21 darjah |
| H1150 | 41 |
|
| AKV 21 darjah |
| H1150M | 75 |
|
| AKV 21 darjah |
| H1150D | 41 |
|
| AKV 21 darjah |
Pemanjangan, A( peratus )
| keadaan | Min | Maks | serupa | Catatan |
|---|
| H900 | 10 |
|
|
|
| H925 | 10 |
|
|
|
| H1025 | 12 |
|
|
|
| H1075 | 13 |
|
|
|
| H1100 | 14 |
|
|
|
| H1150 | 16 |
|
|
|
| H1150M | 18 |
|
|
|
| H1150D | 16 |
|
|
|
Pengurangan kawasan,( peratus )
| keadaan | Min | Maks | serupa | Catatan |
|---|
| H900 | 40 |
|
|
|
| H925 | 44 |
|
|
|
| H1025 | 45 |
|
|
|
| H1075 | 45 |
|
|
|
| H1100 | 45 |
|
|
|
| H1150 | 50 |
|
|
|
| H1150M | 55 |
|
|
|
| H1150D | 50 |
|
|
|
Kekerasan
| keadaan | taip | Min | Maks | serupa | Catatan |
|---|
| A | HRC | 38 |
|
|
|
| A | HB | 363 |
|
|
|
| H900 | HRC | 40 |
|
|
|
| H900 | HB | 388 |
|
|
|
| H925 | HRC | 38 |
|
|
|
| H925 | HB | 375 |
|
|
|
| H1025 | HRC | 35 |
|
|
|
| H1025 | HB | 331 |
|
|
|
| H1075 | HB | 311 |
|
|
|
| H1075 | HRC | 32 |
|
|
|
| H1100 | HRC | 31 |
|
|
|
| H1100 | HB | 302 |
|
|
|
| H1150 | HRC | 28 |
|
|
|
| H1150 | HB | 277 |
|
|
|
| H1150M | HRC | 24 |
|
|
|
| H1150M | HB | 255 |
|
|
|
| H1150D | HRC | 24 |
|
|
|
| H1150D | HB | 255 |
|
|
|
Sifat fizikal gred X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 SAE AMS 5342E (2006)
| Kapasiti haba, cp20 darjah | Catatan |
|---|
| 500 J * kg-1 * K-1 |
|
| Kekonduksian haba, λ | Catatan |
|---|
| 16 W * m-1 * K-1 |
|
| Modulus keanjalan, E | Catatan |
|---|
| 200 IPK |
|
| Ketumpatan | Catatan |
|---|
| 7.85 g/cm3 |
|
| Faktor Pengembangan Linear, 20 darjah | Catatan |
|---|
| 10.9 * 10-6 K-1 |
|
Sifat berkaitan
| Rawatan haba - Menempa dan menggelek pada 1150 - 900 darjah dengan penyejukan di udara |
| Rawatan haba - Penyepuhlindapan pada 1020 - 1055 darjah dengan penyejukan dalam minyak atau udara |
Rawatan haba - Penuaan untuk keadaan tambah P800 pada 760 darjah di udara selama 2j ditambah 620 darjah di udara selama 4j
|
X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 - Butiran
SAE AMS 5342E (2006) Keluli, Tahan Kakisan, Tuangan Pelaburan 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenisasi, Penyelesaian dan Pemendakan Haba Dirawat (H1100) 130 ksi (896 MPa) Kekuatan Tegangan Kerpasan tahan karat keluli keras X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 Digunakan biasanya untuk bahagian yang memerlukan rintangan kakisan dan kekuatan yang baik sehingga 315°C.
Permohonan
Keluli dikeraskan pemendakan tahan karat X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400 ialah salah satu keluli aloi kromium-nikel tahan karat yang paling popular dan paling biasa digunakan dengan bahan tambahan tembaga, pemendakan dikeraskan dengan struktur martensit. Ia dicirikan oleh rintangan kakisan yang tinggi sambil mengekalkan sifat kekuatan tinggi, termasuk kekerasan. Keluli boleh beroperasi dalam julat suhu dari -29 darjah hingga 343 darjah, sambil mengekalkan parameter yang agak baik. Selain itu, bahan dalam gred ini dicirikan oleh kemuluran yang agak baik dan rintangan kakisannya adalah setanding dengan Keluli dikeraskan kerpasan tahan karat X5CrNiCuNb17-4-4, 1.4548, AISI 630, UNS S17400